PA66 Ultramid® A3W BASF GERMANY

Unit Price:US$ 4,940 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PA66 Ultramid® A3W BASF MALAYSIA

Transaction Guarantee:

Supplier Information

Shenzhen Jufengde Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Oil resistant｜Fast forming cycle｜High mobility｜heat-resisting
Application Areas:wheel｜Engine parts｜Laptop case｜bearing
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
remarks			高机械强度、刚度和热稳定性.低温抗冲击性、滑动摩擦性
characteristic			多种工程部件和机械零件（如优质电绝缘材料）及多种特殊应用
Other performance	Test Condition	Test Method	Test Result	Test Unit
elongation	≤0.5%, +23℃，湿		700	Mpa
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	+23℃，干/湿		5.5/NB	KJ/m
Fracture stress (V=50mm/min)	干/湿		85/50	Mpa
Tensile modulus	干/湿		3000/1000	Mpa
Ball Pressure Test	干/湿		160/100	Mpa
impact strength	+23℃，干/湿		75/>140	J
Charpy Notched Impact Strength	+23℃，干/湿		6/20	KJ/m
Tensile creep modulus	1000h,湿		700	Mpa
Elongation at Break	干/湿，V=50mm/min		4.4/20	%
impact strength	-20℃,干		30	J
Tensile yield stress (V=50mm/min)	干/湿		85/50	Mpa
Charpy Notched Impact Strength	+23℃，干/湿		NB/NB	KJ/m
Elongation at Break	干/湿，V=50mm/min		4.4/20	%
Bending modulus	干/湿		3100	Mpa
Impact strength of cantilever beam gap	-30℃,干		6	KJ/m
Tensile modulus		ASTM D638/ISO 527	3000	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	85屈服	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2900	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Temperature index	在20000h/5000h，后拉伸强度下降50%时		121/147	°C
Linear coefficient of thermal expansion	（23-80）℃，Dry		7-10
thermal conductivity	Dry		0.23	W/(m.K)
Maximum operating temperature			>200	°C
specific heat	Dry		1.7	J/(g.K)
Hot deformation temperature	0.45MPa负荷，Dry		220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa负荷，Dry		75	°C
Melting temperature			260	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7-1	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1130
Shrinkage rate		ASTM D955	/0.85	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	K20/P50，干/湿		120/60	KV/mm
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 500
Volume resistivity	干/湿		10	Ω.cm
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 475 M
Loss angle	1MHz，干/湿		0.025/0.2
Dielectric constant	1MHz，干/湿		3.5/7
Surface resistivity	干/湿		10	Ω
Volume resistivity		ASTM D257/IEC 60093	1E 13	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 4630 /MT
Shanghai Huibao/Huibai	US$ 6490 /MT

Supplier Join

Get App

Top

PA66 Ultramid® A3W BASF GERMANY

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index