PA66

PA66 LNP™ LUBRICOMP™ RFL36 SABIC INNOVATIVE US

223

Unit Price:US$ 4,901 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
90MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:wear resistant｜Thermal stability｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Plastic bag
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy		ISO 6603-2	2.50 J
Dart impact	23°C,TotalEnergy	ASTM D3763	8.50 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	55 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.5 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	11700 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	10400 Mpa
tensile strength	Yield	ASTM D638	160 Mpa
	tensile strength	Yield	ISO 527-2/5	168 Mpa
		tensile strength	Break	ASTM D638	160 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	158 Mpa
elongation	Yield	ASTM D638	2.8 %
Tensile strain	Yield	ISO 527-2/5	2.8 %
elongation	Break	ASTM D638	2.8 %
Wear factor	Washer	ASTM D3702Modified	5.00 10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Ring	ASTM D3702Modified	0.250 10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.61
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.67
bending strength	Break,50.0mmSpan	ASTM D790	233 Mpa
	bending strength	Yield,50.0mmSpan	ASTM D790	233 Mpa
	bending strength	bending strength		ISO 178	219 Mpa
Bending modulus		ISO 178	8890 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	9260 Mpa
Tensile strain	Break	ISO 527-2/5	2.8 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	244 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	249 °C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	258 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	260 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	0.40-0.60 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	1.0-3.0 %
Water absorption rate	24hr,50%RH	ASTM D570	0.37 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.58 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 LNP™ LUBRICOMP™ RFL36 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet