PA66 RFL36 SABIC INNOVATIVE US
LNP™ LUBRICOMP™ 
Plastic bag
wear resistant,Thermal stability,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/RFL36
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648249 °C
0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf258 °C
1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af244 °C
0.45MPa,Unannealed,3.20mmASTM D648260 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RFL36
Bending modulus50.0mmSpanASTM D7909260 Mpa
ISO 1788890 Mpa
bending strengthYield,50.0mmSpanASTM D790233 Mpa
ISO 178219 Mpa
Break,50.0mmSpanASTM D790233 Mpa
elongationBreakASTM D6382.8 %
YieldASTM D6382.8 %
Friction coefficientDynamicASTM D3702Modified0.67
StaticASTM D3702Modified0.61
Tensile modulusASTM D63811700 Mpa
ISO 527-2/110400 Mpa
Tensile strainBreakISO 527-2/52.8 %
YieldISO 527-2/52.8 %
tensile strengthBreakISO 527-2/5158 Mpa
YieldASTM D638160 Mpa
YieldISO 527-2/5168 Mpa
BreakASTM D638160 Mpa
Wear factorRingASTM D3702Modified0.250 10^-10in^5-min/ft-lb-hr
WasherASTM D3702Modified5.00 10^-10in^5-min/ft-lb-hr
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RFL36
Shrinkage rateTD：24hrASTM D9551.0-3.0 %
MD：24hrASTM D9550.40-0.60 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.58 %
24hr,50%RHASTM D5700.37 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/RFL36
Dart impact23°C,TotalEnergyASTM D37638.50 J
Impact strength of cantilever beam gap23°CISO 180/1A7.5 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-22.50 J
Suspended wall beam without notch impact strength23°CISO 180/1U55 kJ/m²