PA66 Radiflam® A RV 300 RADIC ITALY

389

Unit Price:US$ 3,750 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	75	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
flammability		FMVSS 302	0	mm/min
Burning wire flammability index	2.0 mm	IEC 60695-2-12	700	°C
UL flame retardant rating	0.8 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	275	Mpa
Bending modulus		ISO 178	8500	Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.9	%
tensile strength	Break	ISO 527-2/1A/5	180	Mpa
Tensile modulus		ISO 527-2/1A/1	9500	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Drying temperature - hot air dryer			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Dew Point - Hot Air Drying Machine			-20	°C
Suggested maximum moisture content			0.15	%
Processing (melt) temperature			280 to 300	°C
Mold temperature			80 to 100	°C
Injection speed			中等偏快
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	260	°C
Vicat softening temperature		ISO 306/B50	245	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	235	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.7	%
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	7.0	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.0	%
density		ISO 1183	1.35	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 0
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Surface resistivity		IEC 60093	1.0E+12	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Guangzhou HuShang Chemical	US$ 5880 /MT

Supplier Join

Get App

Top

PA66 Radiflam® A RV 300 RADIC ITALY

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index