Material Description
- Material Properties:transparent｜High rigidity｜Thermal stability
- Application Areas:transparent｜High rigidity｜Thermal stability
- Color:--
- Grade:Optical grade
Technical Data Sheet
Compare
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 47.0 % |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 141 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 129 °C | |
| vicat | ISO 306/B50 | 148 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 141 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD:4.00mm | 内部方法 | 0.50-0.70 % |
| MD:4.00mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| shrinkage rate | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω | |
| volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω.cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 61.0 Mpa |
| 断裂 | ISO 527-2/50 | 59.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | >50 % | |
| flexural modulus | ISO 178 | 2230 Mpa | |
| bending strength | ISO 178 | 93.0 Mpa | |
| Elongation at break | ASTM D638/ISO 527 | 50 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 66.0 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 6.0 % | |
| flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 96.0 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 120 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.