Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML-1103 TEIJIN JAPAN
PANLITE®
transparent,High rigidity,Thermal stability
transparent,High rigidity,Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| thermal performance | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 129 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 141 °C | |
| HDT | ASTM D648/ISO 75 | 141 ℃（℉） | |
| vicat | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| ISO 306/B50 | 148 °C | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ | ||
| MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| bending strength | ASTM D790/ISO 178 | 96.0 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 屈服 | ISO 527-2/50 | 61.0 Mpa |
| elongation | ASTM D638/ISO 527 | 6.0 % | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | >50 % | |
| Elongation at break | ASTM D638/ISO 527 | 120 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 59.0 Mpa |
| bending strength | ISO 178 | 93.0 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 66.0 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ISO 178 | 2230 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω | |
| volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω.cm | |
| IEC 60093 | >1.0E+15 ohms·cm | ||
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| optical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 47.0 % |
| other | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| shrinkage rate | MD:4.00mm | 内部方法 | 0.50-0.70 % |
| ASTM D955 | 0.50-0.70 % | ||
| TD:4.00mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| ASTM D570/ISO 62 | 0.20 % |