PC/PBT XENOY™  X4830 SABIC INNOVATIVE US

310
  • Unit Price:US$ 3,100 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    113MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜High impact resistance｜Dimensional stability
  • Application Areas:Automotive Applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA12 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA40 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A9.0 kJ/m²
Impact strength of cantilever beam gap0°CISO 180/1A15 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A45 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact-20°C,TotalEnergyASTM D376370.0 J
Dart impact23°C,TotalEnergyASTM D376370.0 J
Multi axis Instrumented Impact EnergyISO 6603-2110 J
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainYieldISO 527-2/504.2 %
elongationBreak3ASTM D638150 %
elongationBreak4ASTM D638140 %
Tensile strainBreakISO 527-2/5120 %
Tensile strainBreakISO 527-2/50110 %
Bending modulus50.0mmSpanASTM D7903100 Mpa
Bending modulusISO 1782900 Mpa
bending strengthISO 17890.0 Mpa
bending strengthYield,50.0mmSpanASTM D79096.0 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelInternal Method30.0 mg
tensile strengthYieldASTM D63860.0 Mpa
tensile strengthYieldISO 527-2/555.0 Mpa
tensile strengthYieldISO 527-2/5061.0 Mpa
tensile strengthBreak3ASTM D63860.0 Mpa
tensile strengthBreak4ASTM D63860.0 Mpa
tensile strengthBreakISO 527-2/560.0 Mpa
tensile strengthBreakISO 527-2/5055.0 Mpa
elongationYieldASTM D6384.5 %
elongationYieldASTM D6384.1 %
Tensile strainYieldISO 527-2/54.1 %
Tensile modulusASTM D6383400 Mpa
Tensile modulusISO 527-2/13200 Mpa
tensile strengthYieldASTM D63856.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648125 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf119 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648106 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af97.0 °C
Vicat softening temperatureASTM D152511133 °C
Vicat softening temperature--ISO 306/B50133 °C
Vicat softening temperature--ISO 306/B120135 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8316E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-30to80°CISO 11359-27.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8318.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-30to80°CISO 11359-29E-05 cm/cm/°C
thermal conductivityISO 83020.20 W/m/K
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate266°C/5.0kgASTM D12387.0 g/10min
Melt Volume Flow Rate (MVR)265°C/5.0kgISO 11336.00 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.70-0.90 %
Water absorption rateSaturation,23°CISO 620.42 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.14 %
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestH358/30ISO 2039-1105 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.