ABS CYCOLAC™ FR15-NA1000 SABIC INNOVATIVE US
243
- Unit Price:US$ 3,779 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜Flame retardant
- Application Areas:small home appliances｜Automotive Applications｜Electrical applications｜composite
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 82.2 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 70.0 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 73.4 °C | |
| vicat | ASTM D15258 | 86.1 °C | |
| -- | ISO 306/B50 | 81.2 °C | |
| -- | ISO 306/B120 | 84.1 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 8.6E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 60.0 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI Str | UL 746 | 60.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 2.5mm | UL 94 | 5VA |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.5 kJ/m² |
| 23°C | ISO 180/1A | 19 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 33.9 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 4.0 g/10min |
| 220°C/5.0kg | ISO 1133 | 10 g/10min | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| MeltViscosity | 200°C,1000sec^-1 | ASTM D3835 | 290 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2340 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 41.4 Mpa |
| 屈服 | ISO 527-2/50 | 41.3 Mpa | |
| 断裂 | ASTM D638 | 35.2 Mpa | |
| 断裂 | ISO 527-2/50 | 31.3 Mpa | |
| elongation | 屈服 | ASTM D638 | 2.3 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 2.1 % |
| elongation | 断裂 | ASTM D638 | 9.0 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 34 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2720 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 71.7 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.