Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS FR15-NA1000 SABIC INNOVATIVE US
CYCOLAC™
small home appliances、Automotive Applications、Electrical applications、composite
UV resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15-NA1000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 33.9 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.5 kJ/m² |
| 23°C | ISO 180/1A | 19 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/FR15-NA1000 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2340 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 41.3 Mpa |
| elongation | 断裂 | ASTM D638 | 9.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 71.7 Mpa |
| elongation | 屈服 | ASTM D638 | 2.3 % |
| tensile strength | 断裂 | ASTM D638 | 35.2 Mpa |
| 屈服 | ASTM D638 | 41.4 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 34 % |
| 屈服 | ISO 527-2/50 | 2.1 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 31.3 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2720 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15-NA1000 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/FR15-NA1000 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/FR15-NA1000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 4.0 g/10min |
| 220°C/5.0kg | ISO 1133 | 10 g/10min | |
| MeltViscosity | 200°C,1000sec^-1 | ASTM D3835 | 290 Pa·s |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15-NA1000 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 84.1 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 8.6E-05 cm/cm/°C |
| vicat | ASTM D15258 | 86.1 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 82.2 °C |
| vicat | -- | ISO 306/B50 | 81.2 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 73.4 °C |
| RTI Str | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 70.0 °C |
| RTI Elec | UL 746 | 60.0 °C |