PC PANLITE® G-3430R TEIJIN JAPAN
236
- Unit Price:US$ 3,029 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:67.2MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜High rigidity｜Good demolding performance
- Application Areas:machine｜Mechanical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 要求达-UL-940V-0级的电器电子元件 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 151 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 148 °C | |
| vicat | ISO 306/B50 | 153 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6E-05 cm/cm/°C | |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| RTI Imp | 1.5mm | UL 746 | 125 °C |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.43mm | UL 94 | HB |
| 0.8mm | UL 94 | V-2 | |
| 3.0mm | UL 94 | V-1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 35 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.43 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.12 % | |
| shrinkage rate | TD:4.00mm | 内部方法 | 0.30-0.50 % |
| MD:4.00mm | 内部方法 | 0.020-0.20 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.12 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| 1MHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 118(12) kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 2.5 % | |
| Tensile modulus | ASTM D638/ISO 527 | 7950(81000) kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 108(1100) kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 7260(74000) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 162(1650) kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2/1 | 8000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 105 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| flexural modulus | ISO 178 | 7100 Mpa | |
| bending strength | ISO 178 | 160 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.