PPO NORYL PPX™  PPX7200U-BK1A363 SABIC INNOVATIVE US

204
  • Unit Price:US$ 4,754 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    30MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Dimensional stability｜High impact｜High rigidity
  • Application Areas:Printer components｜Cold water pipe application｜Water heater
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength-30°C9ISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CASTM D48121400 J/m
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU80 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA12 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA6.0 kJ/m²
Suspended wall beam without notch impact strength23°C9ISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376336.0 J
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span5ASTM D79048.0 Mpa
bending strength--6,7ISO 17848.0 Mpa
Bending modulus--6ISO 1781600 Mpa
Bending modulus50.0 mm Span5ASTM D7901440 Mpa
elongationBreakISO 527-2/50120 %
elongationBreak4ASTM D638130 %
elongationYieldISO 527-2/508.2 %
elongationYield4ASTM D63810 %
tensile strengthBreakISO 527-2/5028.0 Mpa
tensile strengthBreak4ASTM D63827.0 Mpa
tensile strengthYieldISO 527-2/5034.0 Mpa
tensile strengthYield4ASTM D63833.0 Mpa
Tensile modulus--ISO 527-2/11670 Mpa
Tensile modulus--3ASTM D6381240 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature60 to 65 °C
drying time2.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume30 to 70 %
Temperature at the rear of the barrel225 to 275 °C
Temperature in the middle of the barrel240 to 280 °C
Temperature at the front of the material cylinder250 to 290 °C
Spray nozzle temperature260 to 290 °C
Processing (melt) temperature260 to 290 °C
Mold temperature30 to 50 °C
Back pressure0.300 to 0.700 Mpa
Screw speed20 to 100 rpm
Exhaust hole depth0.038 to 0.051 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648110 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64871.0 °C
Vicat softening temperature--ASTM D152510146 °C
Vicat softening temperature--ISO 306/B50103 °C
Vicat softening temperature--ISO 306/B120107 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8319.9E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8311.1E-4 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.60 - 0.80 %
Shrinkage rateFlow : 3.20 mmInternal Method0.60 - 0.80 %
Shrinkage rateFlow 2Internal Method0.060 - 0.080 %
Melt Volume Flow Rate (MVR)260°C/5.0 kgISO 113318.0 cm3/10min
melt mass-flow rate260°C/5.0 kgASTM D123816 g/10 min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.