Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PPO PPX7200U-BK1A363 SABIC INNOVATIVE US
NORYL PPX™
Printer components、Cold water pipe applicati、Water heater
Dimensional stability、High impact、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/PPX7200U-BK1A363 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
Suspended wall beam without notch impact strength | -30°C9 | ISO 180/1U | 无断裂 |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1400 J/m |
Dart impact | 23°C, Total Energy | ASTM D3763 | 36.0 J |
Suspended wall beam without notch impact strength | 23°C9 | ISO 180/1U | 无断裂 |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/PPX7200U-BK1A363 |
---|---|---|---|
tensile strength | 屈服4 | ASTM D638 | 33.0 Mpa |
elongation | 断裂4 | ASTM D638 | 130 % |
Tensile modulus | --3 | ASTM D638 | 1240 Mpa |
Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 1440 Mpa |
elongation | 断裂 | ISO 527-2/50 | 120 % |
bending strength | --6,7 | ISO 178 | 48.0 Mpa |
Flexural modulus | --6 | ISO 178 | 1600 Mpa |
bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 48.0 Mpa |
tensile strength | 断裂 | ISO 527-2/50 | 28.0 Mpa |
屈服 | ISO 527-2/50 | 34.0 Mpa | |
elongation | 屈服 | ISO 527-2/50 | 8.2 % |
屈服4 | ASTM D638 | 10 % | |
tensile strength | 断裂4 | ASTM D638 | 27.0 Mpa |
Tensile modulus | -- | ISO 527-2/1 | 1670 Mpa |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/PPX7200U-BK1A363 |
---|---|---|---|
Shrinkage rate | 流动 2 | 内部方法 | 0.060 - 0.080 % |
横向流动 : 3.20 mm | 内部方法 | 0.60 - 0.80 % | |
Melt volume flow rate | 260°C/5.0 kg | ISO 1133 | 18.0 cm3/10min |
Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.60 - 0.80 % |
melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 16 g/10 min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/PPX7200U-BK1A363 |
---|---|---|---|
Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 9.9E-5 cm/cm/°C |
vicat | -- | ISO 306/B120 | 107 °C |
-- | ASTM D152510 | 146 °C | |
-- | ISO 306/B50 | 103 °C | |
Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm,HDT | ASTM D648 | 110 °C |
Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C |
Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm,HDT | ASTM D648 | 71.0 °C |
injection | Test Condition | Test Method | SABIC INNOVATIVE US/PPX7200U-BK1A363 |
---|---|---|---|
screw speed | 20 to 100 rpm | ||
Suggested maximum moisture content | 0.020 % | ||
Processing (melt) temperature | 260 to 290 °C | ||
drying temperature | 60 to 65 °C | ||
Suggested injection volume | 30 to 70 % | ||
drying time | 2.0 to 4.0 hr | ||
Temperature in the middle of the barrel | 240 to 280 °C | ||
Temperature at the rear of the barrel | 225 to 275 °C | ||
Exhaust hole depth | 0.038 to 0.051 mm | ||
Temperature at the front of the material cylinder | 250 to 290 °C | ||
Back pressure | 0.300 to 0.700 Mpa | ||
Temperature | 30 to 50 °C | ||
Spray nozzle temperature | 260 to 290 °C |