thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 3.20 mm	ASTM D648	79.0 °C
	Heat Deflection Temperature	1.8 MPa, 未退火, 3.20 mm	ASTM D648	75.0 °C
		Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9	ISO 75-2/Ae	80.0 °C
		Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8	ISO 75-2/Af	78.0 °C
vicat	--	ASTM D152510	91.0 °C
vicat	vicat	--	ISO 306/B120	96.0 °C
ball-indentation hardness	85°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	流动 : -40 到 40°C	ASTM E831	1.1E-4 cm/cm/°C
	Linear coefficient of thermal expansion	流动 : 23 到 60°C	ISO 11359-2	9.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	1.1E-4 cm/cm/°C
			Linear coefficient of thermal expansion	横向 : -40°C	ISO 11359-2	1.1E-4 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 23 到 60°C	ISO 11359-2	9.0E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K

optical performance	Test Condition	Test Method	Test Result
refractive index		ISO 489	1.539
transmissivity	2540 µm	ASTM D1003	88.0 %
Haze ratio	2540 µm	ASTM D1003	1.0 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0 mm	UL 94	V-2
Burning wire flammability index	1.0 mm	IEC 60695-2-12	750 °C

Impact resistance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	95.0 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	265°C/2.16 kg	ASTM D1238	15 g/10 min
Melt volume flow rate	265°C/2.16 kg	ISO 1133	15.0 cm3/10min
shrinkage rate	流动 : 3.20 mm	内部方法	0.50 - 0.80 %
shrinkage rate	shrinkage rate	横向流动 : 3.20 mm	内部方法	0.40 - 0.60 %
Water absorption rate	饱和, 23°C	ISO 62	0.050 %
Water absorption rate	Water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.20 %

Electrical performance	Test Method	Test Result
Surface Resistivity	ASTM D257	> 1.0E+15 ohms
volume resistivity	ASTM D257	> 1.0E+15 ohms·cm
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 0

injection	Test Condition	Test Method	Test Result
drying temperature			65 to 75 °C
drying time			3.0 to 5.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 80 %
Temperature at the rear of the barrel			240 to 250 °C
Temperature in the middle of the barrel			240 to 260 °C
Temperature at the front of the material cylinder			245 to 265 °C
Spray nozzle temperature			245 to 265 °C
Processing (melt) temperature			245 to 265 °C
mold temperature			45 to 60 °C
Back pressure			0.200 to 0.500 Mpa
screw speed			20 to 100 rpm
Exhaust hole depth			0.013 to 0.020 mm

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	1520 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	1600 Mpa
tensile strength	屈服3	ASTM D638	47.0 Mpa
	tensile strength	屈服	ISO 527-2/50	55.0 Mpa
		tensile strength	断裂3	ASTM D638	46.0 Mpa
		tensile strength	tensile strength	断裂	ISO 527-2/50	54.0 Mpa
elongation	屈服3	ASTM D638	5.0 %
	elongation	屈服	ISO 527-2/50	> 5.0 %
		elongation	断裂3	ASTM D638	150 %
		elongation	elongation	断裂	ISO 527-2/50	> 200 %
flexural modulus	50.0 mm 跨距4	ASTM D790	1680 Mpa
flexural modulus	flexural modulus	--5	ISO 178	1700 Mpa
bending strength	--5,6	ISO 178	78.0 Mpa
bending strength	bending strength	屈服, 50.0 mm 跨距4	ASTM D790	71.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.