PC/PET X8300 SABIC INNOVATIVE NANSHA
XYLEX™ 
Electronic field、Electrical field
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
Dart impact23°C, Total EnergyASTM D376395.0 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
Shore hardness邵氏 D, 10 秒ASTM D224073
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
Tensile modulus--2ASTM D6381520 Mpa
tensile strength 屈服3ASTM D63847.0 Mpa
elongation断裂3ASTM D638150 %
断裂ISO 527-2/50> 200 %
Flexural modulus--5ISO 1781700 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79071.0 Mpa
--5,6ISO 17878.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7901680 Mpa
tensile strength 断裂ISO 527-2/5054.0 Mpa
屈服ISO 527-2/5055.0 Mpa
elongation屈服ISO 527-2/50> 5.0 %
屈服3ASTM D6385.0 %
tensile strength 断裂3ASTM D63846.0 Mpa
Tensile modulus--ISO 527-2/11600 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
Volume resistivityASTM D257> 1.0E+15 ohms·cm
Surface ResistivityASTM D257> 1.0E+15 ohms
Compared to the Leakage Tracking Index (CTI)UL 746PLC 0
optical performance Test ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
transmissivity2540 µmASTM D100388.0 %
refractive indexISO 4891.539
Haze ratio2540 µmASTM D10031.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
UL flame retardant rating3.0 mmUL 94V-2
Burning wire flammability index1.0 mmIEC 60695-2-12750 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
Water absorption rate平衡, 23°C, 50% RHISO 620.20 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.40 - 0.60 %
Melt volume flow rate265°C/2.16 kgISO 113315.0 cm3/10min
melt mass-flow rate265°C/2.16 kgASTM D123815 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.50 - 0.80 %
Water absorption rate饱和, 23°CISO 620.050 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8311.1E-4 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDTISO 75-2/Ae80.0 °C
Linear coefficient of thermal expansion流动 : 23 到 60°CISO 11359-29.0E-5 cm/cm/°C
横向 : 23 到 60°CISO 11359-29.0E-5 cm/cm/°C
ball-indentation hardness85°CIEC 60695-10-2通过
Linear coefficient of thermal expansion横向 : -40°CISO 11359-21.1E-4 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D64879.0 °C
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDTISO 75-2/Af78.0 °C
vicat--ISO 306/B12096.0 °C
thermal conductivityISO 83020.23 W/m/K
vicat--ASTM D15251091.0 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8311.1E-4 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D64875.0 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/X8300
screw speed20 to 100 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature245 to 265 °C
drying temperature65 to 75 °C
Suggested injection volume40 to 80 %
drying time3.0 to 5.0 hr
Temperature in the middle of the barrel240 to 260 °C
Temperature at the rear of the barrel240 to 250 °C
Exhaust hole depth0.013 to 0.020 mm
Temperature at the front of the material cylinder245 to 265 °C
Back pressure0.200 to 0.500 Mpa
Temperature45 to 60 °C
Spray nozzle temperature245 to 265 °C