ABS/PMMA

ABS/PMMA STAREX® BF-0677HF Samsung Cheil South Korea

370

Unit Price:US$ 2,106 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Aging resistance｜High impact resistance
Application Areas:Automotive components｜Casters｜Electronic and electrical components｜Shell
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	88 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	120 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	80.0 Mpa
bending strength	bending strength		ASTM D790	69.0 Mpa
Bending modulus		ISO 178	2600 Mpa
Bending modulus	Bending modulus		ASTM D790	2500 Mpa
Tensile strain	Break	ISO 527-2/50	20 %
elongation	Break	ASTM D638	15 %
tensile strength	Break	ISO 527-2/50	38.0 Mpa
	tensile strength	Break	ASTM D638	29.0 Mpa
		tensile strength	Yield	ISO 527-2/50	53.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	47.0 Mpa
Tensile modulus		ISO 527-2/50	2600 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	93.0 °C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	88.0 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	84.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	76.0 °C
Vicat softening temperature	--	ISO 306/B50	95.096.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	98.099.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	ASTM D955	0.40 %
melt mass-flow rate	220°C/10.0kg	ISO 1133	19 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	19 g/10min
density		ISO 1183	1.13 g/cm³
density	density		ASTM D792	1.13 g/cm³
Shrinkage rate	MD:3.20mm	ISO 2577	0.40 %
	Shrinkage rate	TD:3.20mm	ISO 2577	0.50 %
	Shrinkage rate	Shrinkage rate	TD：3.20mm	ASTM D955	0.50 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	116
Pencil hardness		JISK5401	H
Rockwell hardness	R-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top