Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PMMA BF-0677HF Samsung Cheil South Korea
STAREX®
Automotive components、Casters、Electronic and electrical、Shell
High temperature resistan、Aging resistance、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/BF-0677HF |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 88 J/m |
| 23°C | ISO 180/1A | 10 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 120 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/BF-0677HF |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 116 |
| R级 | ASTM D785 | 114 | |
| Hardness | JISK5401 | H |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/BF-0677HF |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 53.0 Mpa |
| elongation | 断裂 | ASTM D638 | 15 % |
| Tensile modulus | ISO 527-2/50 | 2600 Mpa | |
| bending strength | ISO 178 | 80.0 Mpa | |
| Flexural modulus | ISO 178 | 2600 Mpa | |
| bending strength | ASTM D790 | 69.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 29.0 Mpa |
| 屈服 | ASTM D638 | 47.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| Flexural modulus | ASTM D790 | 2500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 38.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/BF-0677HF |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/BF-0677HF |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40 % |
| TD:3.20mm | ISO 2577 | 0.50 % | |
| TD：3.20mm | ASTM D955 | 0.50 % | |
| density | ASTM D792 | 1.13 g/cm³ | |
| ISO 1183 | 1.13 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 19 g/10min |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.40 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 19 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/BF-0677HF |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 76.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 84.0 °C | |
| vicat | -- | ISO 306/B120 | 98.099.0 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 88.0 °C |
| vicat | -- | ISO 306/B50 | 95.096.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 93.0 °C |