PA66/PTFE LNP™ LUBRICOMP™ RBL-4036 SABIC INNOVATIVE US

498

Unit Price:US$ 5,580 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low extract｜Wear resistance｜Corrosion resistance
Application Areas:Lampholder cover｜building materials｜Gear cover
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	--	ISO 6603-2	1.34	J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	5.60	J
Suspended wall beam without notch impact strength	23°C6	ISO 180/1U	27	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	440	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-2/5	8.3	%
Bending modulus	50.0mmSpan4	ASTM D790	3740	Mpa
Bending modulus	Bending modulus	--5	ISO 178	3570	Mpa
bending strength		ISO 178	107	Mpa
elongation	Break3	ASTM D638	10	%
elongation	elongation	Yield3	ASTM D638	8.5	%
tensile strength	Break	ISO 527-2/5	64.0	Mpa
Wear factor	Washer	ASTM D3702Modified	41.0	10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Ring	ASTM D3702Modified	8.00	10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.44
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.47
tensile strength	Break3	ASTM D638	64.0	Mpa
Tensile modulus	--	ISO 527-2/1	3930	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	3990	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:-30to30°C	ASTM D696	6.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-30to30°C	ASTM D696	8.3E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan7	ISO 75-2/Af	73.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	83.0	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan7	ISO 75-2/Bf	203	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	236	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.58	%
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.41	%
Shrinkage rate	TD:24hr	ASTM D955	1.0-3.0	%
Shrinkage rate	Shrinkage rate	MD:24hr	ASTM D955	2.0-4.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Tenamo (Guangdong)	US$ 5460 /MT

Supplier Join

Get App

Top

PA66/PTFE LNP™ LUBRICOMP™ RBL-4036 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index