Plastic Raw Materials
PBT

PBT Crastin®  S620F20 DuPont, European Union

270
  • Unit Price:US$ 3,343 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    18.3MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

Filling analysisTest ConditionTest MethodTest Result
Melt density1.11 g/cm³
Top out temperature170 °C
SpecificHeatCapacity of Melt2100 J/kg/°C
ThermalConductivityofMelt0.21 W/m/K
impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U140 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U70 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A4.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A5.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA4.5 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA3.5 kJ/m²
flammabilityTest ConditionTest MethodTest Result
FMVSS flammabilityFMVSS302SE/NBR
UL flame retardant rating0.8mmUL 94,IEC60695-11-10,-20HB
UL flame retardant rating1.5mmUL 94,IEC60695-11-10,-20HB
Extreme Oxygen IndexISO 4589-222 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainYieldISO 527-28.0 %
tensile strengthYieldISO 527-259.0 Mpa
Tensile modulusISO 527-22600 Mpa
Nominal tensile fracture strainISO 527-230 %
bending strengthISO 17888.0 Mpa
Tensile creep modulus1000hrISO 899-11800 Mpa
Tensile creep modulus1hrISO 899-12600 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A60.0 °C
Hot deformation temperature1.8MPa,AnnealedISO 75-2/A60.0 °C
Hot deformation temperature0.45MPa,AnnealedISO 75-2/B180 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B145 °C
Vicat softening temperatureISO 306/B50175 °C
Melting temperatureISO 11357-3225 °C
Crystallization peak temperatureISO 11357-3192 °C
Linear coefficient of thermal expansionMDISO 11359-21.3E-04 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-21.3E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
StickinessISO 307130 cm³/g
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.20 %
Water absorption rateSaturation,23°C,2.00mmISO 620.40 %
Shrinkage rateMDISO 294-41.7 %
Shrinkage rateTDISO 294-41.6 %
melt mass-flow rate250°C/2.16kgISO 113319 g/10min
densityISO 11831.31 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strengthIEC 60243-126 KV/mm
Relative permittivity100HzIEC 602503.80
Relative permittivity1MHzIEC 602503.20
Dissipation factor100HzIEC 602502E-03
Dissipation factor1MHzIEC 602500.020
Compared to the anti leakage trace indexIEC 60112PLC 0
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.