Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S620F20 DuPont, European Union
Crastin®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 无断裂 |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.5 kJ/m² |
| -30°C | ISO180/1U | 70 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 5.0 kJ/m² |
| 23°C | ISO180/1A | 4.0 kJ/m² | |
| 23°C | ISO180/1U | 140 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 30 % | |
| Tensile creep modulus | 1hr | ISO899-1 | 2600 Mpa |
| Tensile stress | 屈服 | ISO527-2 | 59.0 Mpa |
| Bending stress | ISO178 | 88.0 Mpa | |
| Tensile strain | 屈服 | ISO527-2 | 8.0 % |
| Tensile modulus | ISO527-2 | 2600 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1800 Mpa |
| Electrical performance | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| Dissipation Factor | 1MHz | IEC60250 | 0.020 |
| CTI | IEC60112 | 600 V | |
| 1MHz | IEC60250 | 3.20 | |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC60243-1 | 26 KV/mm | |
| 100Hz | IEC60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC60250 | 2E-03 |
| flammability | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | SE/NBR | |
| UL flame retardant rating | 0.8mm | UL94,IEC60695-11-10,-20 | HB |
| 1.5mm | UL94,IEC60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO4589-2 | 22 % |
| Filling analysis | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| Ejection Temperature | 170 °C | ||
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| SpecificHeatCapacity of Melt | 2100 J/kg/°C | ||
| Melt density | 1.11 g/cm³ |
| physical property | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO1133 | 19 g/10min |
| Shrinkage rate | TD | ISO294-4 | 1.6 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.40 % |
| viscosity number | ISO307 | 130 cm³/g | |
| Shrinkage rate | MD | ISO294-4 | 1.7 % |
| density | ISO1183 | 1.31 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | DuPont, European Union/S620F20 |
|---|---|---|---|
| TD | ISO11359-2 | 1.3E-04 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 145 °C | |
| vicat | ISO306/B50 | 175 °C | |
| 0.45MPa,退火 | ISO75-2/B | 180 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 60.0 °C | |
| Melting temperature 3 | ISO11357-3 | 225 °C | |
| 1.8MPa,退火 | ISO75-2/A | 60.0 °C | |
| MD | ISO11359-2 | 1.3E-04 cm/cm/°C | |
| Crystallization peak temperature 3 | ISO11357-3 | 192 °C |