PC/PBT

PC/PBT XENOY™ 6620U-BK1066 SABIC INNOVATIVE SHANGHAI

266

Unit Price:US$ 2,669 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
98MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜Low temperature impact resistance
Application Areas:Plastic bag｜Lighting applications｜Household daily necessities
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	72 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	51 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	54 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	56.3 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	1700 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	1780 Mpa
Tensile strain	Break	ISO 527-2/50	19 %
elongation	Break	ASTM D638	150 %
Tensile strain	Yield	ISO 527-2/50	3.9 %
elongation	Yield	ASTM D638	4.2 %
tensile strength	Break	ISO 527-2/50	31.7 Mpa
tensile strength	tensile strength	Yield	ASTM D638	43.7 Mpa
Tensile modulus		ISO 527-2/1	1830 Mpa
Tensile modulus	Tensile modulus		ASTM D638	1780 Mpa
tensile strength	Break	ASTM D638	32.9 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	41.1 Mpa
bending strength		ISO 178	60.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	63.6 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	75.0 °C
RTI Imp		UL 746	75.0 °C
RTI Elec		UL 746	75.0 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	9.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.9E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	98.9 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	60.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	50.5 °C
Vicat softening temperature		ASTM D152510	123 °C
	Vicat softening temperature	--	ISO 306/B50	119 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	122 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	ISO 62	0.14 %
Shrinkage rate	TD：3.20mm	Internal Method	1.6-1.8 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	1.6-1.8 %
Specific volume		ASTM D792	0.835 cm³/g
melt mass-flow rate	266°C/5.0kg	ASTM D1238	22 g/10min
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	17.1 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	HAI	UL 746	PLC 0
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Arc resistance		ASTM D495	PLC 5
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Hot wire ignition	HWI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ 6620U-BK1066 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet