Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 6620U-BK1066 SABIC INNOVATIVE SHANGHAI
XENOY™
Plastic bag、Lighting applications、Household daily necessiti
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/6620U-BK1066 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 72 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 56.3 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 51 kJ/m² |
| 23°C | ISO 180/1A | 54 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/6620U-BK1066 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/6620U-BK1066 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1830 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.2 % |
| tensile strength | 断裂 | ASTM D638 | 32.9 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.9 % |
| tensile strength | 断裂 | ISO 527-2/50 | 31.7 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1780 Mpa |
| Tensile modulus | ASTM D638 | 1780 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 41.1 Mpa |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 63.6 Mpa |
| ISO 178 | 60.0 Mpa | ||
| Flexural modulus | ISO 178 | 1700 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 43.7 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 19 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/6620U-BK1066 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/6620U-BK1066 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.6-1.8 % |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 22 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 1.6-1.8 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.14 % |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 17.1 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/6620U-BK1066 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 60.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 9.9E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 9.9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 98.9 °C |
| vicat | ASTM D152510 | 123 °C | |
| RTI Str | UL 746 | 75.0 °C | |
| vicat | -- | ISO 306/B120 | 122 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 119 °C |
| RTI Imp | UL 746 | 75.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 50.5 °C |
| RTI Elec | UL 746 | 75.0 °C |