PA6 Grilon®  TS-V0 EMS-CHEMIE SWITZERLAND

253
  • Unit Price:US$ 8,270 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Glass fiber reinforced｜Thermal stability
  • Application Areas:Automotive Applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

Other performanceTest ConditionTest MethodTest Result
Flammability levelUL 94干燥｜V-0
Flammability levelUL 94干燥｜V-0
Extreme Oxygen IndexISO 4589-2干燥｜35
mechanical propertiesTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA干燥｜3.0 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA调节后｜3.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA干燥｜4.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA调节后｜15 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU干燥｜70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU调节后｜- kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU干燥｜75 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU调节后｜100 kJ/m²
Tensile modulusISO 527-2干燥｜3600 Mpa
Tensile modulusISO 527-2调节后｜1600 Mpa
tensile strengthYield干燥｜85 Mpa
tensile strengthYield调节后｜50 Mpa
tensile strengthBreakISO 527-2干燥｜75 Mpa
tensile strengthBreakISO 527-2调节后｜50 Mpa
Tensile strainBreakISO 527-2干燥｜4.0 %
Tensile strainBreakISO 527-2调节后｜15 %
Nominal tensile fracture strainISO 527-2干燥｜10 %
Nominal tensile fracture strainISO 527-2调节后｜＞50 %
thermal performanceTest ConditionTest MethodTest Result
Continuous use temperature--3ISO 2578干燥｜100 -120 °C
Continuous use temperature--4Internal Method干燥｜200 °C
Melting temperatureISO 11357-3干燥｜260 °C
Linear coefficient of thermal expansionMDISO 11359-2干燥｜7.0E-5 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-2干燥｜9.0E-5 cm/cm/°C
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/A干燥｜210 °C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/C干燥｜70 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateTDISO 294-4干燥｜0.80 %
Shrinkage rateMDISO 294-4干燥｜0.70 %
Water absorption rateSaturation, 23°CISO 62干燥｜8.0 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 62干燥｜2.5 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093调节后｜1.0E+10 ohms
Volume resistivityIEC 60093干燥｜1.0E+13 ohms·cm
Volume resistivityIEC 60093调节后｜1.0E+11 ohms·cm
Dielectric strengthIEC 60243-1干燥｜28 KV/mm
Dielectric strengthIEC 60243-1调节后｜26 KV/mm
Relative permittivity100 Hz干燥｜3.00
Relative permittivity100 Hz调节后｜8.00
Relative permittivity1 MHz干燥｜3.00
Relative permittivity1 MHz调节后｜4.00
Dissipation factor100 Hz干燥｜5.0E-3
Dissipation factor100 Hz调节后｜0.15
Dissipation factor1 MHz干燥｜0.015
Dissipation factor1 MHz调节后｜0.070
Compared to the anti leakage trace indexIEC 60112 V
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.