PA6 TS-V0 EMS-CHEMIE SWITZERLAND
Grilon®
Automotive Applications
Glass fiber reinforced、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/TS-V0 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 干燥｜35 | |
| Flammability level | UL 94 | 干燥｜V-0 |
| Electrical performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/TS-V0 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 调节后｜26 KV/mm | |
| Volume resistivity | IEC 60093 | 调节后｜1.0E+11 ohms·cm | |
| relative permittivity | 1 MHz | 调节后｜4.00 | |
| 100 Hz | 调节后｜8.00 | ||
| Dissipation Factor | 100 Hz | 调节后｜0.15 | |
| 1 MHz | 调节后｜0.070 | ||
| Surface Resistivity | IEC 60093 | 调节后｜1.0E+10 ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/TS-V0 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 调节后｜1600 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 调节后｜＞50 % | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 调节后｜3.0 kJ/m² |
| 23°C | ISO 179/1eA | 调节后｜15 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2 | 调节后｜15 % |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 调节后｜- kJ/m² |
| tensile strength | 断裂 | ISO 527-2 | 调节后｜50 Mpa |
| 屈服 | 调节后｜50 Mpa | ||
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 调节后｜100 kJ/m² |
| physical property | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/TS-V0 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 干燥｜2.5 % |
| Shrinkage rate | TD | ISO 294-4 | 干燥｜0.80 % |
| MD | ISO 294-4 | 干燥｜0.70 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 干燥｜8.0 % |
| Thermal performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/TS-V0 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 干燥｜260 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 干燥｜7.0E-5 cm/cm/°C |
| Continuous use temperature | --4 | 内部方法 | 干燥｜200 °C |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/A | 干燥｜210 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 干燥｜9.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/C | 干燥｜70 °C |
| Continuous use temperature | --3 | ISO 2578 | 干燥｜100 -120 °C |