PC/PET XYLEX™ X5230 BK1G338 SABIC INNOVATIVE US
202
- Unit Price:US$ 3,786 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:32MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High heat resistance｜Filler: Mineral filler
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 100 °C |
| vicat | -- | ISO 306/B50 | 137 °C |
| -- | ISO 306/B120 | 140 °C | |
| Linear coefficient of thermal expansion | MD：-30到80°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |
| TD：-30to80°C | ISO 11359-2 | 9.7E-05 cm/cm/°C | |
| TD:-30到80°C | ISO 11359-2 | 9.7E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 8.0 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 120 kJ/m² |
| 23°C | ISO 180/1U | 140 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 28 g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 24.0 cm3/10min |
| shrinkage rate | MD2 | 内部方法 | 0.50-0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.42 % |
| 平衡,23°C,50%RH | ISO 62 | 0.14 % | |
| shrinkage rate | MD2 | 内部方法 | 0.50-0.60 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 53.0 Mpa |
| 断裂 | ISO 527-2/5 | 34.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.4 % |
| 断裂 | ISO 527-2/5 | 21 % | |
| flexural modulus | ISO 178 | 3820 Mpa | |
| bending strength | ISO 178 | 90.0 Mpa | |
| Tensile modulus | ISO 527-2/1 | 3990 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.