PC/PET X5230 BK1G338 SABIC INNOVATIVE US
XYLEX™
Automotive Applications
Flame retardant,High heat resistance,Filler: Mineral filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X5230 BK1G338 |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 100 °C |
Linear coefficient of thermal expansion | MD:-30to80°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |
TD:-30to80°C | ISO 11359-2 | 9.7E-05 cm/cm/°C | |
TD:-30to80°C | ISO 11359-2 | 9.7E-05 cm/cm/°C | |
Vicat softening temperature | -- | ISO 306/B120 | 140 °C |
-- | ISO 306/B50 | 137 °C |
mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X5230 BK1G338 |
---|---|---|---|
Bending modulus | ISO 178 | 3820 Mpa | |
bending strength | ISO 178 | 90.0 Mpa | |
Tensile modulus | ISO 527-2/1 | 3990 Mpa | |
Tensile strain | Break | ISO 527-2/5 | 21 % |
Yield | ISO 527-2/5 | 3.4 % | |
tensile strength | Break | ISO 527-2/5 | 34.0 Mpa |
Yield | ISO 527-2/5 | 53.0 Mpa |
Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X5230 BK1G338 |
---|---|---|---|
melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 28 g/10min |
Melt Volume Flow Rate (MVR) | 265°C/5.0kg | ISO 1133 | 24.0 cm3/10min |
Shrinkage rate | MD2 | Internal Method | 0.50-0.60 % |
Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.14 % |
Saturation,23°C | ISO 62 | 0.42 % |
impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/X5230 BK1G338 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
23°C | ISO 180/1A | 8.0 kJ/m² | |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 140 kJ/m² |
-30°C | ISO 180/1U | 120 kJ/m² |