ABS DENKA TE-10S DENKA JAPAN
252
- Unit Price:US$ 2,641 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜transparent｜High mobility
- Application Areas:Electronic field｜Automotive sector｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Vicat softening temperature | ASTM D1525/ISO R306 | 87 ℃（℉） | |
| Hot deformation temperature | 1.80MPa | ISO 75-1 | 70 °C |
| Vicat softening temperature | 50N | ISO 306(JIS K7206) | 87 °C |
| Combustibility | UL 94 | HB |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Total Light Transmittance | 2mmt | ISO 13468-1(JIS K7361) | 91 % |
| turbidity | 2mmt | ISO 14782(JIS 7136) | 1.5 % |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 200℃,49N | ISO 1133(JIS K7210) | 1.7 g/10min |
| 220℃,98N | ISO 1133(JIS K7210) | 25 g/10min | |
| density | 23℃ | ISO 1183(JIS K7112) | 1092 kg/m3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | |
| Shrinkage rate | ASTM D955 | 0.5 % | |
| DENKA Method | 0.5 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 46 | |
| Bending modulus | ASTM D790/ISO 178 | 2000(MPa) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 63(MPa) kg/cm²(MPa)[Lb/in²] | |
| Tensile stress | 50mm/min | ISO 527-1 | 42 Mpa |
| Bending modulus | 2m/min | ISO 178(JIS K7171) | 2000 Mpa |
| bending strength | 2mm/min | ISO 178(JIS K7171) | 63 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179(JIS K7111) | 15 kJ/m² |
| Rockwell hardness | 23℃ | ISO 2039-2(JIS K7202) | 46 M |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.