Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TE-10S DENKA JAPAN
DENKA
Electronic field、Automotive sector、Electrical field
High temperature resistan、transparent、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/TE-10S |
|---|---|---|---|
| melt mass-flow rate | 200℃,49N | ISO 1133(JIS K7210) | 1.7 g/10min |
| density | 23℃ | ISO 1183(JIS K7112) | 1092 kg/m3 |
| melt mass-flow rate | 220℃,98N | ISO 1133(JIS K7210) | 25 g/10min |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/TE-10S |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 63(MPa) kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2000(MPa) kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | 23℃ | ISO 2039-2(JIS K7202) | 46 M |
| Flexural modulus | 2m/min | ISO 178(JIS K7171) | 2000 Mpa |
| bending strength | 2mm/min | ISO 178(JIS K7171) | 63 Mpa |
| Rockwell hardness | ASTM D785 | 46 | |
| Tensile stress | 50mm/min | ISO 527-1 | 42 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179(JIS K7111) | 15 kJ/m² |
| optical performance | Test Condition | Test Method | DENKA JAPAN/TE-10S |
|---|---|---|---|
| Total Light Transmittance | 2mmt | ISO 13468-1(JIS K7361) | 91 % |
| Haze ratio | 2mmt | ISO 14782(JIS 7136) | 1.5 % |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/TE-10S |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5 % | |
| density | ASTM D792/ISO 1183 | 1.09 |
| physical property | Test Condition | Test Method | DENKA JAPAN/TE-10S |
|---|---|---|---|
| Shrinkage rate | DENKA Method | 0.5 % |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/TE-10S |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| vicat | ASTM D1525/ISO R306 | 87 ℃（℉） | |
| 50N | ISO 306(JIS K7206) | 87 °C | |
| Heat distortion temperature | 1.80MPa | ISO 75-1 | 70 °C |
| combustibility | UL 94 | HB |