Material Description
- Material Properties:High rigidity｜Glass fiber reinforced
- Application Areas:Engineering accessories｜Shell｜electrical machinery｜printed circuit board
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa，Unannealed 66 psi, Unannealed | ISO 75-2/B | 200 °C |
| 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 95 °C | |
| melting temperature | ISO 11357-3 | 223 °C | |
| Linear coefficient of thermal expansion | MD：23~80℃ MD：23 to 80℃ | ISO 11359-2 | 7.0E-5 - 8.0E-5 1/℃ |
| specific heat | 1500 J/kg/℃ | ||
| thermal conductivity | DIN 52612 | 0.27 W/m/K | |
| Temperature index - at 50% loss of tensile strength | ---- 66 | IEC 60216 | 120 °C |
| Temperature index - at 51% loss of tensile strength | ---- 77 | IEC 60216 | 130 °C |
| maximum service temperature | short cycle operation | 200 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C -30°C | ISO 179/1eU | 24 kJ/m² |
| 23℃23°C | ISO 179/1eU | 35 kJ/m² |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | HB | |
| 1.6 mm | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | 0.70 to 0.80 g/cm³ | ||
| Melt volume flow rate | 250℃，2.16 kg250℃/2.16 kg | ISO 1133 | 9 cm3/10min |
| Water absorption rate | Saturation，23℃ Saturation, 73°F | ISO 62 | 0.4 % |
| Equilibrium，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 0.2 % | |
| viscosity number | ISO 307 | 113 cm³/g | |
| shrinkage rate | MD：自由的free, longitudinal | 1.7 % | |
| TD：自由的free, transverse | 1.7 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 10000000000000 ohms | |
| volume resistivity | IEC 60093 | 10000000000000000 ohms·cm | |
| relative permittivity | 100 Hz100 Hz | IEC 60250 | 3.8 |
| 1 MHz1 MHz | IEC 60250 | 3.8 | |
| Dissipation Factor | 100 Hz100 Hz | IEC 60250 | 0.0012 |
| 1 MHz1 MHz | IEC 60250 | 0.019 | |
| Compared to the Leakage Tracking Index (CTI) | Solution A Solution A | IEC 60112 | V |
| Solution B Solution B | IEC 60112 | V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 165 Mpa |
| Tensile modulus | ISO 527-2 | 4000 Mpa | |
| tensile strength | Break Break | ISO 527-2 | 50 Mpa |
| Tensile strain | Break Break | ISO 527-2 | 5 % |
| Tensile creep modulus | 1000 hr1000 hr5 | ISO 899-1 | 2200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.