PC/ABS IUPILON™ MB-1800 MITSUBISHI ENGINEERING JAPAN
223
- Unit Price:US$ 3,275 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility
- Application Areas:Electronic and Electrical Applications｜Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0(1.2mm) | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 81 ℃（℉） |
| HDT | ASTM D648/ISO 75 | 89 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | - mm/mm.℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 89.0 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 81.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.2mm | UL 94 | V-0 |
| 2.0mm | UL 94 | 5VB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.18 | |
| shrinkage rate | ASTM D955 | 0.3-0.5 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 14 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % | |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 14 g/10min |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 14.0 cm3/10min |
| shrinkage rate | TD:3.20mm | 0.30-0.50 % | |
| MD:3.20mm | 0.30-0.50 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at break | ASTM D638/ISO 527 | 92 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2800 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 60 % | |
| flexural modulus | ASTM D790/ISO 178 | 2800 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 95 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 4.0 % | |
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 60.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Nominal tensile fracture strain | ISO 527-2 | 92 % | |
| flexural modulus | ISO 178 | 2800 Mpa | |
| bending strength | ISO 178 | 95.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.