PC/ABS MB-1800 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and Electrical Applications,Shell
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB-1800 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB-1800 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 95 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 2800 kg/cm²(MPa)[Lb/in²] | |
| Nominal tensile fracture strain | ISO 527-2 | 92 % | |
| bending strength | ISO 178 | 95.0 Mpa | |
| Flexural modulus | ISO 178 | 2800 Mpa | |
| elongation | ASTM D638/ISO 527 | 60 % | |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Tensile modulus | ASTM D638/ISO 527 | 2800 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 4.0 % | |
| tensile strength | 屈服 | ISO 527-2 | 60.0 Mpa |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB-1800 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3-0.5 % | |
| density | ASTM D792/ISO 1183 | 1.18 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 14 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB-1800 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| 1.2mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB-1800 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.30-0.50 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 14.0 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.30-0.50 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 14 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB-1800 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0(1.2mm) | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 89 ℃（℉） |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 89.0 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 81.0 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | - mm/mm.℃ |