Material Description

Material Properties:Middle flow｜Biocompatibility｜Steam sterilization
Application Areas:Medical devices｜Medical and nursing supplies
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	30	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	10.0	J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	30	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	50.0mmSpan	ASTM D790	5500	Mpa
Tensile strain	Break	ISO 527-2/5	4.0	%
elongation	Break	ASTM D638	6.0	%
Tensile strain	Yield	ISO 527-2/5	4.0	%
elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ISO 527-2/5	115	Mpa
	tensile strength	Break	ASTM D638	115	Mpa
		tensile strength	Yield	ISO 527-2/5	115	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	114	Mpa
Tensile modulus		ISO 527-2/1	4500	Mpa
Tensile modulus	Tensile modulus		ASTM D638	4680	Mpa
Bending modulus		ISO 178	4500	Mpa
bending strength		ISO 178	185	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	160	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：23to150°C	ISO 11359-2	2.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	3.2E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	217	°C
	Vicat softening temperature	--	ISO 306/B50	212	°C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	223	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	205	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	205	°C
RTI Str		UL 746	170	°C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	6E-05	cm/cm/°C
RTI Elec		UL 746	170	°C
RTI Imp		UL 746	170	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.60	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	1.0	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.60	%
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	9.00	cm3/10min
melt mass-flow rate	200°C/3.8kg	ASTM D1238	5.0	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 4
Dielectric strength	3.20mm,in Oil	IEC 60243-1	15	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PEI ULTEM™ HU2100 7H8D479 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index