PEI HU2100 7H8D479 SABIC INNOVATIVE US
ULTEM™
Medical devices、Medical and nursing suppl
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HU2100 7H8D479 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 30 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 30 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 10.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU2100 7H8D479 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 4500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 115 Mpa |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.0 % |
| tensile strength | 断裂 | ASTM D638 | 115 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 5500 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 115 Mpa |
| Tensile modulus | ASTM D638 | 4680 Mpa | |
| elongation | 断裂 | ASTM D638 | 6.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 160 Mpa |
| ISO 178 | 185 Mpa | ||
| Flexural modulus | ISO 178 | 4500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| tensile strength | 屈服 | ASTM D638 | 114 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU2100 7H8D479 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 15 KV/mm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HU2100 7H8D479 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.60 % |
| Melt volume flow rate | 360°C/5.0kg | ISO 1133 | 9.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.60 % |
| 饱和,23°C | ISO 62 | 1.0 % | |
| melt mass-flow rate | 200°C/3.8kg | ASTM D1238 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU2100 7H8D479 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 217 °C |
| Linear coefficient of thermal expansion | TD：23to150°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 6E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 212 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.2E-05 cm/cm/°C |
| vicat | ASTM D152510 | 223 °C | |
| RTI Imp | UL 746 | 170 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 205 °C |
| RTI Str | UL 746 | 170 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 205 °C |
| Linear coefficient of thermal expansion | MD：23到150°C | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| RTI Elec | UL 746 | 170 °C |