PA66 66G30HR DOMO CHEM GERMANY
237
- Unit Price:US$ 3,899 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:90MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Hydrolysis resistance|Glass fiber reinforced|filler|Glass fiber reinforced material|30%|Filler by weight|filler|Glass fiber reinforced material|30%|Filler by weight
- Application Areas:Automotive sector|Electronic field|Electrical field|Household appliances|Industrial machinery|Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
ISO | ISO 1874 | PA 66.MHW.14-100.GF30 | |
UL flame retardant rating | 0.8 mm | UL 94 | HB |
Burning rate | FMVSS 302 | < 100 mm/min |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
bending strength | ISO 178 | 250 Mpa | |
Bending modulus | ISO 178 | 8500 Mpa | |
Tensile strain | Break | ISO 527-2/5 | 3.0 % |
tensile strength | Break | ISO 527-2/5 | 190 Mpa |
Tensile modulus | ISO 527-2/1 | 10000 Mpa |
injection | Test Condition | Test Method | Test Result |
---|---|---|---|
Mold temperature | 90 to 110 °C | ||
Processing (melt) temperature | 270 to 290 °C | ||
drying time | 2.0 to 4.0 hr | ||
drying temperature | 75 to 85 °C |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Melting temperature | ISO 11357-3 | 262 °C | |
Vicat softening temperature | ISO 306/B50 | 255 °C | |
Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 250 °C |
0.45 MPa, Unannealed | ISO 75-2/B | 255 °C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Stickiness | 96% H2SO4 | ISO 307 | 145 cm³/g |
Shrinkage rate | Flow : 23°C, 72hr | ISO 2577 | 0.20 - 0.40 % |
横向Flow : 23°C, 72hr | ISO 2577 | 0.70 - 0.90 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Compared to the anti leakage trace index | Solution A | IEC 60112 | V |
Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
Surface resistivity | IEC 60093 | 1.0E+13 ohms |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.