PA66 66G30HR DOMO CHEM GERMANY
--
Automotive sector,Electronic field,Electrical field,Household appliances,Industrial machinery,Fitness equipment
Hydrolysis resistance,Glass fiber reinforced,filler,Glass fiber reinforced ma,30%,Filler by weight,filler,Glass fiber reinforced ma,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 10000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 190 Mpa |
| bending strength | ISO 178 | 250 Mpa | |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.0 % |
| Electrical performance | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1.0E+13 ohms |
| flammability | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| burning rate | FMVSS 302 | < 100 mm/min | |
| UL flame retardant rating | 0.8 mm | UL 94 | HB |
| ISO 9660 | ISO 1874 | PA 66.MHW.14-100.GF30 |
| physical property | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| Shrinkage rate | 流量 : 23°C, 72小时 | ISO 2577 | 0.20 - 0.40 % |
| viscosity number | 96% H2SO4 | ISO 307 | 145 cm³/g |
| Shrinkage rate | 横向流量 : 23°C, 72小时 | ISO 2577 | 0.70 - 0.90 % |
| Thermal performance | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 255 °C |
| vicat | ISO 306/B50 | 255 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 250 °C |
| injection | Test Condition | Test Method | DOMO CHEM GERMANY/66G30HR |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 270 to 290 °C | ||
| drying temperature | 75 to 85 °C | ||
| Temperature | 90 to 110 °C |