ABS Novodur® HD M203FC WT018646 INEOS GERMANY
365
- Unit Price:US$ 5,927 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility
- Application Areas:medical care｜Shell｜Medical/nursing supplies
- Color:--
- Grade:Medical grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 31 g/10min | |
| ISO 294-4 | 0.4-0.7 % | ||
| Melt volume flow rate | ISO 1133 | 31.0 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 110 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 294 | 240 °C | |
| injection speed | ISO 294 | 240 mm/sec | |
| burning rate | ISO 3795 | 60 mm/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 46 Mpa | |
| elongation at break | ISO 527-2 | 2.6 % | |
| ISO 527-2 | >=15 % | ||
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| bending strength | ISO 178 | 70 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 15 kJ/m² | |
| ISO 179/1eA | 7 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 110 kJ/m² | |
| ISO 179/1eU | 90 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 15 kJ/m² | |
| ISO 180/1A | 7 kJ/m² | ||
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| tensile strength | ISO 527-2 | 46.0 Mpa | |
| Tensile strain | ISO 527-2 | 2.6 % | |
| ISO 527-2 | >15 % | ||
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 70.0 Mpa | |
| ball-indentation hardness | ISO 2039-1 | 105 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 90 kJ/m² | |
| ISO 179 | 110 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| GWIT | IEC 60695-2-12 | 700 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | IEC 60250 | 2.9 1MHz | |
| IEC 60250 | 3 100HZ | ||
| Dissipation Factor | IEC 60250 | 0.05 | |
| IEC 60250 | 0.09 | ||
| IEC 60112 | 600 V | ||
| Volume resistivity | IEC 60093 | 1E+13 Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+15 Ω.cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| relative permittivity | IEC 60250 | 3.00 | |
| IEC 60250 | 2.90 | ||
| Dissipation Factor | IEC 60250 | 5E-03 | |
| IEC 60250 | 9E-03 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 98 °C | |
| ISO 75-2/Af | 94 °C | ||
| vicat | ISO 306/A50 | 99 °C | |
| Heat distortion temperature | ISO 75-2/B | 98.0 °C | |
| ISO 75-2/A | 94.0 °C | ||
| vicat | ISO 306/B50 | 99.0 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.