Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS HD M203FC WT018646 INEOS GERMANY
Novodur®
medical care、Shell、Medical/nursing supplies
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| melting temperature | ISO 294 | 240 °C | |
| burning rate | ISO 3795 | 60 mm/min | |
| injection speed | ISO 294 | 240 mm/sec |
| Impact resistance | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 90 kJ/m² |
| 23°C | ISO 179 | 110 kJ/m² |
| hardness | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| dielectric strength | 1.00mm | IEC 60243-1 | 35 KV/mm |
| dielectric constant | IEC 60250 | 2.9 1MHz | |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| dielectric strength | 1.50mm | IEC 60243-1 | 35 KV/mm |
| Surface Resistivity | IEC 60093 | 1E+15 Ω.cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Volume resistivity | IEC 60093 | 1E+13 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Dissipation Factor | IEC 60250 | 0.09 | |
| dielectric constant | IEC 60250 | 3 100HZ | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| ball-indentation hardness | ISO 2039-1 | 105 Mpa | |
| tensile strength | 屈服，23°C | ISO 527-2 | 46 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 110 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7 kJ/m² |
| Tensile strain | 断裂,23°C | ISO 527-2 | >15 % |
| bending strength | 23°C | ISO 178 | 70 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7 kJ/m² |
| bending strength | ISO 178 | 70.0 Mpa | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 kJ/m² |
| tensile strength | 屈服,23°C | ISO 527-2 | 46.0 Mpa |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| elongation at break | 屈服，23°C | ISO 527-2 | 2.6 % |
| Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.6 % |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 90 kJ/m² |
| elongation at break | 23°C | ISO 527-2 | >=15 % |
| Flame retardant performance | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| GWIT | 2.00mm | IEC 60695-2-12 | 700 °C |
| physical property | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| melt mass-flow rate | 线性收缩率 | ISO 294-4 | 0.4-0.7 % |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| melt mass-flow rate | 220℃/10.0Kg | ISO 1133 | 31 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 31.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | INEOS GERMANY/HD M203FC WT018646 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 94 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 94.0 °C | |
| vicat | ISO 306/B50 | 99.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 98 °C |
| vicat | 5.10kg | ISO 306/A50 | 99 °C |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/B | 98.0 °C |