PBT

PBT VALOX™ 420HP-1001 SABIC INNOVATIVE NANSHA

228

Unit Price:US$ 5,408 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜dimensional stability ｜High rigidity｜high strength｜heat-resisting
Application Areas:Lawn equipment｜Garden equipment｜Industrial applications｜Automotive External Parts｜Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive interior parts｜Casters｜Household goods｜Petroleum Applications｜Natural gas supplies｜sporting goods｜Textile application｜Lighting applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	45 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	45 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	8.00 J

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/5	125 Mpa
tensile strength	tensile strength	Yield	ASTM D638	120 Mpa
Tensile modulus		ISO 527-2/1	9300 Mpa
Tensile modulus	Tensile modulus		ASTM D638	9300 Mpa
Tensile strain	Yield	ASTM D638	3.0 %
tensile strength	Break	ASTM D638	120 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	125 Mpa
Tensile strain	Yield	ISO 527-2/5	2.0 %
	Tensile strain	Break	ASTM D638	3.0 %
	Tensile strain	Tensile strain	Break	ISO 527-2/5	2.0 %
Bending modulus	50.0mmSpan	ASTM D790	7580 Mpa
Bending modulus	Bending modulus		ISO 178	8500 Mpa
bending strength		ISO 178	195 Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	189 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	2.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	215 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	215 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.2E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	220 °C
	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	216 °C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	217 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	203 °C
Vicat softening temperature		ASTM D152514	215 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	223 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	204 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD：--5	Internal Method	0.60-0.90 %
	Shrinkage rate	MD：3.20mm	Internal Method	0.30-0.80 %
		Shrinkage rate	MD：--4	Internal Method	0.30-0.70 %
			Shrinkage rate	MD：--3	Internal Method	0.30-0.50 %
			Shrinkage rate	Shrinkage rate	MD：--2	Internal Method	0.50-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %
	Water absorption rate	Saturation,23°C	ISO 62	0.26 %
	Water absorption rate	Water absorption rate	24hr	ASTM D570	0.060 %
Shrinkage rate	TD：3.20mm	Internal Method	0.50-1.0 %
	Shrinkage rate	TD：--4	Internal Method	0.50-1.0 %
	Shrinkage rate	Shrinkage rate	TD：--3	Internal Method	0.40-0.60 %
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	13.0 cm3/10min
melt mass-flow rate	250°C/2.16kg	ASTM D1238	17 g/10min
Specific volume		ASTM D792	0.650 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	ASTM D150	0.020
Dissipation factor	Dissipation factor	100Hz	ASTM D150	2E-03
Dielectric constant	1MHz	ASTM D150	3.70
Volume resistivity		ASTM D257	>3.2E+16 ohms·cm
Dielectric strength	1.60mm,in Oil	ASTM D149	25 KV/mm
Dielectric strength	Dielectric strength	3.20mm,inAir	ASTM D149	19 KV/mm
Dielectric constant	100Hz	ASTM D150	3.80

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118

Supplementary Information	Test Condition	Test Method	Test Result
Filling material		ASTM D229	30 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ 420HP-1001 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet