PBT 420HP-1001 SABIC INNOVATIVE NANSHA
VALOX™
Lawn equipment、Garden equipment、Industrial applications、Automotive External Parts、Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive interior parts、Casters、Household goods、Petroleum Applications、Natural gas supplies、sporting goods、Textile application、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 45 kJ/m² |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
Supplementary Information | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
filler | ASTM D229 | 30 % |
hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 118 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 9300 Mpa | |
tensile strength | Yield | ASTM D638 | 120 Mpa |
断裂 | ISO 527-2/5 | 125 Mpa | |
Tensile strain | 屈服 | ISO 527-2/5 | 2.0 % |
bending strength | Break,50.0mmSpan | ASTM D790 | 189 Mpa |
Flexural modulus | 50.0mmSpan | ASTM D790 | 7580 Mpa |
Tensile strain | Break | ASTM D638 | 3.0 % |
tensile strength | 屈服 | ISO 527-2/5 | 125 Mpa |
Tensile modulus | ASTM D638 | 9300 Mpa | |
tensile strength | Break | ASTM D638 | 120 Mpa |
Tensile strain | Yield | ASTM D638 | 3.0 % |
bending strength | ISO 178 | 195 Mpa | |
Flexural modulus | ISO 178 | 8500 Mpa | |
Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
Volume resistivity | ASTM D257 | >3.2E+16 ohms·cm | |
Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
dielectric constant | 1MHz | ASTM D150 | 3.70 |
dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
dielectric constant | 100Hz | ASTM D150 | 3.80 |
dielectric strength | 1.60mm,在油中 | ASTM D149 | 25 KV/mm |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.30-0.80 % |
Water absorption rate | 24hr | ASTM D570 | 0.060 % |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.50-1.0 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
饱和,23°C | ISO 62 | 0.26 % | |
Shrinkage rate | MD:--2 | 内部方法 | 0.50-0.80 % |
MD:--3 | 内部方法 | 0.30-0.50 % | |
MD:--4 | 内部方法 | 0.30-0.70 % | |
Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 17 g/10min |
Shrinkage rate | TD:--3 | 内部方法 | 0.40-0.60 % |
TD:--4 | 内部方法 | 0.50-1.0 % | |
TD:--5 | 内部方法 | 0.60-0.90 % | |
Specific volume | ASTM D792 | 0.650 cm³/g |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/420HP-1001 |
---|---|---|---|
Linear coefficient of thermal expansion | TD:-40到40°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
MD:-40到40°C | ASTME831 | 2.5E-05 cm/cm/°C | |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 220 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,6.40mm,HDT | ASTM D648 | 216 °C |
0.45MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Bf | 217 °C | |
vicat | -- | ISO 306/B120 | 215 °C |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
vicat | ASTM D152514 | 215 °C | |
-- | ISO 306/A50 | 223 °C | |
-- | ISO 306/B50 | 215 °C | |
Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Af | 204 °C |
1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 203 °C |