PBT

PBT CELANEX® 3300-2 ED3002 CELANESE USA

259

Unit Price:US$ 3,747 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
41.35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜30% enhancement
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30℃	ISO 179/1eU	45 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179/1eU	46 KJ/m
bending strength	23℃	ISO 178	210 Mpa
Bending modulus	23℃	ISO 178	9700 Mpa
Elongation at Break	5mm/min	ISO 527-2/1A	2.5 %
tensile strength	5mm/min	ISO 527-2/1A	130 Mpa
Tensile modulus	1mm/min	ISO 527-2/1A	9200 Mpa
Rockwell hardness		ISO 2039-2	90 M
Impact strength of cantilever beam gap	23℃	ISO 180/1A	7.5 KJ/m
Charpy Notched Impact Strength	-30℃	ISO 179/1eA	8.5 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179/1eA	8.5 KJ/m

thermal performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
Extreme Oxygen Index		ISO 4589	20 %
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1 E-4/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	0.25 E-4/℃
Vicat softening temperature		ISO 306	220 °C
Hot deformation temperature	8.0Mpa	ISO 75-1/-2	150 °C
Hot deformation temperature	Hot deformation temperature	0.45Mpa	ISO 75-1/-2	225 °C
Melting temperature		ISO 11357-1	225 °C
Glass transition temperature		ISO 11357-1	60 °C
Hot deformation temperature	1.8Mpa	ISO 75-1/-2	205 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23℃,50%相对湿度	ISO 62	0.2 %
Water absorption rate	Water absorption rate	23℃,Saturation	ISO 62	0.4 %
Shrinkage rate	Across Flow	ISO 294-4	0.7-0.9 %
Shrinkage rate	Shrinkage rate	Across Flow	ISO 294-4	0.3-0.5 %
Melt Volume Flow Rate (MVR)		ISO 1133	17 CM
density		ISO 1183	1530 kg/m

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	1MHz	IEC 60250	4.1
Volume resistivity	Volume resistivity	100Hz	IEC 6250	4.5
Dielectric dissipation factor	100Hz	IEC 60250	22 E-4
Dielectric dissipation factor	Dielectric dissipation factor	1MHz	IEC 60250	160 E-4
Volume resistivity		IEC 60093	＞1E13 ohm.m
Surface resistivity		IEC 60093	＞1E15 Ohm
Dielectric strength		IEC 60243-1	31 KV/mm
Compared to the Leakage Traceability Index (CTI)		IEC 60112	425

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT CELANEX® 3300-2 ED3002 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet