PBT 3300-2 ED3002 CELANESE USA
CELANEX®
Automotive sector
Glass fiber reinforced、30% enhancement
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/3300-2 ED3002 |
|---|---|---|---|
| tensile strength | 5mm/min | ISO 527-2/1A | 130 Mpa |
| elongation at break | 5mm/min | ISO 527-2/1A | 2.5 % |
| Flexural modulus | 23℃ | ISO 178 | 9700 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 7.5 KJ/m |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 8.5 KJ/m |
| -30℃ | ISO 179/1eA | 8.5 KJ/m | |
| 23℃ | ISO 179/1eU | 46 KJ/m | |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 9200 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eU | 45 KJ/m |
| Rockwell hardness | ISO 2039-2 | 90 M | |
| bending strength | 23℃ | ISO 178 | 210 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/3300-2 ED3002 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| Volume resistivity | 100Hz | IEC 6250 | 4.5 |
| 1MHz | IEC 60250 | 4.1 | |
| Dielectric dissipation factor | 100Hz | IEC 60250 | 22 E-4 |
| 1MHz | IEC 60250 | 160 E-4 | |
| Surface Resistivity | IEC 60093 | ＞1E15 Ohm | |
| Volume resistivity | IEC 60093 | ＞1E13 ohm.m | |
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 425 |
| physical property | Test Condition | Test Method | CELANESE USA/3300-2 ED3002 |
|---|---|---|---|
| Water absorption rate | 23℃,50%相对湿度 | ISO 62 | 0.2 % |
| Shrinkage rate | 横向 | ISO 294-4 | 0.7-0.9 % |
| Melt volume flow rate | ISO 1133 | 17 CM | |
| Water absorption rate | 23℃,饱和 | ISO 62 | 0.4 % |
| Shrinkage rate | 纵向 | ISO 294-4 | 0.3-0.5 % |
| density | ISO 1183 | 1530 kg/m |
| Thermal performance | Test Condition | Test Method | CELANESE USA/3300-2 ED3002 |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-1 | 60 °C | |
| Limiting Oxygen Index | ISO 4589 | 20 % | |
| Heat distortion temperature | 0.45Mpa，HDT | ISO 75-1/-2 | 225 °C |
| 1.8Mpa，HDT | ISO 75-1/-2 | 205 °C | |
| 8.0Mpa，HDT | ISO 75-1/-2 | 150 °C | |
| vicat | ISO 306 | 220 °C | |
| melting temperature | ISO 11357-1 | 225 °C | |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1 E-4/℃ |
| 纵向 | ISO 11359-2 | 0.25 E-4/℃ | |
| UL flame retardant rating | UL 94 | HB |