PA6

PA6 Durethan® BKV20FN01 000000 LANXESS GERMANY

264

Unit Price:US$ 6,277 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Heat aging
Application Areas:Instrument casing｜Electronic and electrical enclosure｜switch｜Laptop case｜Lighting applications｜Office equipment｜Connector
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	40 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	0.8mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	750 °C
Extreme Oxygen Index		ISO 4589-2	34 %
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ISO 527-2/5	3.0 %
Bending modulus	23°C	ISO 178/A	7200 Mpa
bending strength	3.5%Strain	ISO 178/A	-- Mpa
	bending strength	23°C	ISO 178	170 Mpa
	bending strength	bending strength	FlexuralStrainatFlexuralStrength5(23°C)		3.2 %
Tensile modulus	23°C	ISO 527-2/1	7960 Mpa
tensile strength	Break,23°C	ISO 527-2/5	110 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	218 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
Vicat softening temperature		ISO 306/B120	205 °C
Melting temperature		ISO 11357-3	222 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	37.0 cm3/10min
Shrinkage rate	TD:260°C,2.00mm2	ISO 294-4	0.60 %
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.20 %
		Shrinkage rate	MD:260°C,2.00mm2	ISO 294-4	0.30 %
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.10 %
Water absorption rate	Saturation,23°C	ISO 62	5.3 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.6 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	8.6E+15 ohms
Volume resistivity	23°C	IEC 60093	5.3E+17 ohms·cm
Compared to the anti leakage trace index	CTI	UL 746	PLC 0

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA6.GFHR.12-080.GF18;ISO1043-PAGFFR(30+40+72)

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Durethan® BKV20FN01 000000 LANXESS GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet