PPO NORYL™ N190X-701 SABIC INNOVATIVE SHANGHAI
311
- Unit Price:US$ 3,515 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:PPO XYRON™ 240Z ASAHI JAPAN
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent｜High temperature resistance
- Application Areas:Automotive components｜Illuminating lamp
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 20 g/10 min | |
| Melt volume flow rate | ISO 1133 | 23.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % | |
| Water absorption rate | ASTM D570 | 0.080 % | |
| Outdoor applicability | UL 746C | f1 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | V-0 | ||
| UL 94 | 5VA | ||
| Limiting Oxygen Index | ASTM D2863 | 39 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2580 Mpa | |
| ISO 527-2/1 | 2600 Mpa | ||
| tensile strength | ASTM D638 | 60.0 Mpa | |
| ISO 527-2/50 | 58.0 Mpa | ||
| ASTM D638 | 47.0 Mpa | ||
| ISO 527-2/50 | 50.0 Mpa | ||
| elongation | ASTM D638 | 3.6 % | |
| ISO 527-2/50 | 3.2 % | ||
| ASTM D638 | 9.0 % | ||
| ISO 527-2/50 | 9.2 % | ||
| Flexural modulus | ASTM D790 | 2500 Mpa | |
| ASTM D790 | 2300 Mpa | ||
| ISO 178 | 2350 Mpa | ||
| bending strength | ISO 178 | 87.0 Mpa | |
| ASTM D790 | 98.0 Mpa | ||
| ASTM D790 | 91.0 Mpa | ||
| Taber abraser | ASTM D1044 | 76.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 720 J/m | |
| Dart impact | ASTM D3763 | 50.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.8E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| dielectric constant | ASTM D150 | 2.74 | |
| ASTM D150 | 2.60 | ||
| Dissipation Factor | ASTM D150 | 0.013 | |
| ASTM D150 | 5.5E-3 | ||
| arc resistance | ASTM D495 | PLC 7 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| High arc combustion index (HAI) | UL 746 | PLC 2 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 75 to 80 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 215 to 265 °C | ||
| Temperature in the middle of the barrel | 225 to 270 °C | ||
| Temperature at the front of the material cylinder | 240 to 275 °C | ||
| Spray nozzle temperature | 250 to 275 °C | ||
| Processing (melt) temperature | 250 to 275 °C | ||
| Temperature | 55 to 75 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 20 to 100 rpm | ||
| Exhaust hole depth | 0.038 to 0.051 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 95.0 °C | |
| ISO 75-2/Bf | 95.0 °C | ||
| ASTM D648 | 78.0 °C | ||
| ASTM D648 | 86.0 °C | ||
| ISO 75-2/Af | 82.0 °C | ||
| vicat | ASTM D15259 | 104 °C | |
| ISO 306/B120 | 107 °C | ||
| Linear coefficient of thermal expansion | ASTM E831 | 7.7E-5 cm/cm/°C | |
| ASTM E831 | 8.1E-5 cm/cm/°C | ||
| thermal conductivity | ASTM C177 | 0.24 W/m/K | |
| RTI Elec | UL 746 | 95.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.