PPO N190X-701 SABIC INNOVATIVE SHANGHAI

NORYL™

Automotive components,Illuminating lamp

transparent,High temperature resistan

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Rockwell hardness	R 级	ASTM D785	120

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Hot deformation temperature	0.45 MPa, 未退火, 3.20 mm	ASTM D648	95.0 °C
		1.8 MPa, 未退火, 6.40 mm	ASTM D648	86.0 °C
		1.8 MPa, 未退火, 3.20 mm	ASTM D648	78.0 °C
		0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8	ISO 75-2/Bf	95.0 °C
		1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8	ISO 75-2/Af	82.0 °C
Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	8.1E-5 cm/cm/°C
Linear coefficient of thermal expansion		流动 : -40 到 40°C	ASTM E831	7.7E-5 cm/cm/°C
RTI		UL 746	95.0 °C
RTI Elec		UL 746	95.0 °C
RTI Imp		UL 746	80.0 °C
thermal conductivity		ASTM C177	0.24 W/m/K
Vicat softening temperature	--	ISO 306/B120	107 °C
Vicat softening temperature		--	ASTM D15259	104 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Bending modulus	--6	ISO 178	2350 Mpa
		100 mm 跨距5	ASTM D790	2300 Mpa
		50.0 mm 跨距4	ASTM D790	2500 Mpa
bending strength	屈服, 50.0 mm 跨距4	ASTM D790	98.0 Mpa
		屈服, 100 mm 跨距5	ASTM D790	91.0 Mpa
		--6,7	ISO 178	87.0 Mpa
elongation	屈服	ISO 527-2/50	3.2 %
		屈服3	ASTM D638	3.6 %
		断裂3	ASTM D638	9.0 %
		断裂	ISO 527-2/50	9.2 %
Taber abraser	1000 Cycles, 1000 g, CS-17 转轮	ASTM D1044	76.0 mg
Tensile modulus	--2	ASTM D638	2580 Mpa
Tensile modulus		--	ISO 527-2/1	2600 Mpa
tensile strength	断裂	ISO 527-2/50	50.0 Mpa
		断裂3	ASTM D638	47.0 Mpa
		屈服	ISO 527-2/50	58.0 Mpa
		屈服3	ASTM D638	60.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Arc resistance		ASTM D495	PLC 7
Compared to the anti leakage trace index		UL 746	PLC 1
Dielectric constant	100 kHz	ASTM D150	2.60
Dielectric constant		100 Hz	ASTM D150	2.74
Dielectric strength	3.20 mm, in Oil	ASTM D149	19 KV/mm
Dissipation factor	100 kHz	ASTM D150	5.5E-3
Dissipation factor		100 Hz	ASTM D150	0.013
High arc combustion index		UL 746	PLC 2
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 2
Volume resistivity		ASTM D257	1.8E+16 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	20 g/10 min
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	23.0 cm3/10min
Outdoor applicability		UL 746C	f1
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.080 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Dart impact	23°C, Total Energy	ASTM D3763	50.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	720 J/m

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Extreme Oxygen Index		ASTM D2863	39 %
UL flame retardant rating	3.0 mm	UL 94	5VA
		1.0 mm	UL 94	HB
		1.5 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/N190X-701
Back pressure			0.300 to 0.700 Mpa
drying temperature			75 to 80 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.038 to 0.051 mm
Mold temperature			55 to 75 °C
Processing (melt) temperature			250 to 275 °C
Screw speed			20 to 100 rpm
Spray nozzle temperature			250 to 275 °C
Suggested injection volume			30 to 70 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			240 to 275 °C
Temperature at the rear of the barrel			215 to 265 °C
Temperature in the middle of the barrel			225 to 270 °C