PC LEXAN™ HPX8R NA8A005T SABIC INNOVATIVE US
129
- Unit Price:US$ 4,886 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:26MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Easy to demould｜Biocompatibility
- Application Areas:Medical field｜medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 35 g/10min | |
| Melt volume flow rate | ISO 1133 | 33.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.40-0.80 % | |
| 内部方法 | 0.40-0.80 % | ||
| Water absorption rate | ISO 62 | 0.12 % | |
| ISO 62 | 0.093 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 90 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | ASTM D1003 | 82.0 % | |
| Haze ratio | ASTM D1003 | 3.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 825 °C | |
| IEC 60695-2-13 | 850 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 30 kJ/m² | |
| ISO 180/1A | 60 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 79.0 J | |
| Charpy Notched Impact Strength | ISO 179/1eA | 30 kJ/m² | |
| ISO 179/1eA | 60 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| ISO 527-2/1 | 2400 Mpa | ||
| tensile strength | ASTM D638 | 60.0 Mpa | |
| ISO 527-2/50 | 59.0 Mpa | ||
| ASTM D638 | 58.0 Mpa | ||
| ISO 527-2/50 | 56.6 Mpa | ||
| elongation | ASTM D638 | 5.8 % | |
| Tensile strain | ISO 527-2/50 | 5.4 % | |
| elongation | ASTM D638 | 120 % | |
| Tensile strain | ISO 527-2/50 | 120 % | |
| Flexural modulus | ASTM D790 | 2360 Mpa | |
| ISO 178 | 2250 Mpa | ||
| bending strength | ISO 178 | 92.9 Mpa | |
| ASTM D790 | 99.2 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 121 °C | |
| ISO 75-2/Af | 118 °C | ||
| vicat | ASTM D152510 | 138 °C | |
| ISO 306/B50 | 138 °C | ||
| ISO 306/B120 | 140 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 6.5E-05 cm/cm/°C | |
| ISO 11359-2 | 6.5E-05 cm/cm/°C | ||
| ASTME831 | 7.4E-05 cm/cm/°C | ||
| ISO 11359-2 | 7.4E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.