PC HPX8R NA8A005T SABIC INNOVATIVE US
LEXAN™
Medical field,medical care
High mobility,Easy to demould,Biocompatibility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 79.0 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 30 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 30 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 60 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 90 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.8 % |
| tensile strength | 断裂 | ASTM D638 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.4 % |
| tensile strength | 断裂 | ISO 527-2/50 | 56.6 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2360 Mpa |
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 59.0 Mpa |
| elongation | 断裂 | ASTM D638 | 120 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 99.2 Mpa |
| ISO 178 | 92.9 Mpa | ||
| Flexural modulus | ISO 178 | 2250 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 3.0 % |
| transmissivity | 2540µm | ASTM D1003 | 82.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 825 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 33.0 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.093 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 35 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 140 °C |
| Linear coefficient of thermal expansion | TD：-40to95°C | ASTME831 | 7.4E-05 cm/cm/°C |
| MD：-40到95°C | ASTME831 | 6.5E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 138 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 118 °C |
| vicat | ASTM D152510 | 138 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| RTI Str | UL 746 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 121 °C |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.4E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 130 °C |