K(Q) 3G46 BASF GERMANY
282
- Unit Price:US$ 4,836 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.02 g/cm³ | |
| ISO 1183 | 1.02 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 11 g/10min | |
| Melt volume flow rate | ISO 1133 | 12.0 cm3/10min | |
| Shrinkage rate | ASTM D955 | 0.65 % | |
| ISO 294-4 | 0.30-1.0 % | ||
| Water absorption rate | ASTM D570 | 0.070 % | |
| ISO 62 | 0.070 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ASTM D2240 | 75 | |
| ISO 868 | 65 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | ASTM D1003 | 0.20 % | |
| refractive index | ASTM D542 | 1.573 | |
| ISO 489 | 1.573 | ||
| transmissivity | ASTM D1003 | 91.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1640 Mpa | |
| ISO 527-2 | 1550 Mpa | ||
| tensile strength | ASTM D638 | 25.5 Mpa | |
| ISO 527-2 | 27.0 Mpa | ||
| Tensile strain | ISO 527-2 | 2.0 % | |
| elongation | ASTM D638 | 220 % | |
| Nominal tensile fracture strain | ISO 527-2 | 180 % | |
| Flexural modulus | ASTM D790 | 1330 Mpa | |
| ISO 178 | 1550 Mpa | ||
| bending strength | ASTM D790 | 27.2 Mpa | |
| 31.0 Mpa | |||
| ISO 178 | 31.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 3.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak | |
| Impact strength of cantilever beam gap | ASTM D256 | 32 J/m | |
| ISO 180/A | 2.0 kJ/m² | ||
| ISO 180/A | 3.0 kJ/m² | ||
| InstrumentedDartImpact | ASTM D3763 | 20.1 J |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ISO 527-3 | 180 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | >1.0E+14 ohms | |
| IEC 60093 | 1E+15 ohms | ||
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm | ||
| dielectric constant | ASTM D150 | 2.50 | |
| IEC 60250 | 2.50 | ||
| Dissipation Factor | IEC 60250 | 3E-04 | |
| IEC 60250 | 8E-04 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 75.6 °C | |
| ISO 75-2/B | 75.0 °C | ||
| ASTM D648 | 60.0 °C | ||
| ISO 75-2/A | 58.0 °C | ||
| vicat | ASTM D15253 | 87.8 °C | |
| ISO 306/A50 | 81.0 °C | ||
| ISO 306/B50 | 51.0 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 1.3E-04 cm/cm/°C | |
| ISO 11359-2 | 6.0E-5to9.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.