K(Q)胶 3G46 BASF GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 32 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| InstrumentedDartImpact | Totalenergy | ASTM D3763 | 20.1 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 3.0 kJ/m² |
| -30°C | ISO 180/A | 2.0 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 75 |
| 邵氏D | ISO 868 | 65 |
| film | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| elongation | 断裂 | ISO 527-3 | 180 % |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1640 Mpa | |
| ISO 527-2 | 1550 Mpa | ||
| elongation | 断裂 | ASTM D638 | 220 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 27.0 Mpa |
| Flexural modulus | ISO 178 | 1550 Mpa | |
| bending strength | ASTM D790 | 27.2 Mpa | |
| 5.0%应变 | 31.0 Mpa | ||
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.0 % |
| bending strength | -- | ISO 178 | 31.0 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 25.5 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 180 % |
| Flexural modulus | ASTM D790 | 1330 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric constant | 100Hz | IEC 60250 | 2.50 |
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+14 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-04 |
| dielectric constant | 1.00mm,1MHz | ASTM D150 | 2.50 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 8E-04 |
| optical performance | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| transmissivity | 550nm | ASTM D1003 | 91.0 % |
| refractive index | ASTM D542 | 1.573 | |
| Haze ratio | ASTM D1003 | 0.20 % | |
| refractive index | ISO 489 | 1.573 |
| physical property | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 11 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.65 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 0.070 % |
| Shrinkage rate | ISO 294-4 | 0.30-1.0 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.070 % |
| density | ASTM D792 | 1.02 g/cm³ | |
| ISO 1183 | 1.02 g/cm³ | ||
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 12.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/3G46 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 60.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 75.6 °C | |
| vicat | ASTM D15253 | 87.8 °C | |
| -- | ISO 306/A50 | 81.0 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 58.0 °C |
| vicat | -- | ISO 306/B50 | 51.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-04 cm/cm/°C |
| MD | ISO 11359-2 | 6.0E-5to9.0E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/B | 75.0 °C |