PC LEXAN™ EXL9414T 7B1D086T SABIC INNOVATIVE US
183
- Unit Price:US$ 3,863 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:97MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High ductility at low temperature
- Application Areas:Plastic bag｜Quick charging phone case
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Horizontal: -40 to 95 ° C | ASTME831 | 8E-05 cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 121 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 116 °C | |
| Flow: -40 to 95 ° C | ASTME831 | 6.7E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO 11359-2 | 6.7E-05 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 内部方法 | 84.0 % | |
| Haze ratio | 内部方法 | 3.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-1 | |
| UL 94 | V-0 | ||
| Limiting Oxygen Index | ISO 4589-2 | 36 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --7 | ISO 178 | 2120 Mpa | |
| --8 | ISO 178 | 88.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 92.0 Mpa | |
| yield | ASTM D638 | 57.6 Mpa | |
| ISO 527-2/50 | 56.8 Mpa | ||
| fracture | ASTM D638 | 59.1 Mpa | |
| ISO 527-2/50 | 55.3 Mpa | ||
| yield | ASTM D638 | 5.6 % | |
| ISO 527-2/50 | 5.4 % | ||
| fracture | ASTM D638 | 120 % | |
| ISO 527-2/50 | 110 % | ||
| 50.0mm span | ASTM D790 | 2180 Mpa | |
| --1 | ASTM D638 | 2180 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 60 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| -30°C | ASTM D256 | 710 J/m | |
| 23°C | ASTM D256 | 820 J/m | |
| -30°C | ISO 180/1A | 55 kJ/m² | |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Dart impact | ASTM D3763 | 75.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 1.19 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 13 g/10min | |
| Melt volume flow rate | ISO 1133 | 12.0 cm3/10min | |
| shrinkage rate | 内部方法 | 0.40-0.80 % | |
| Water absorption rate | ISO 62 | 0.12 % | |
| ISO 62 | 0.090 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.