Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9414T 7B1D086T SABIC INNOVATIVE US
LEXAN™
Plastic bag,Quick charging phone case
High mobility,High ductility at low tem
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9414T 7B1D086T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 75.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| 23°C | ASTM D256 | 820 J/m | |
| -30°C | ASTM D256 | 710 J/m | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| -30°C | ISO 180/1A | 55 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9414T 7B1D086T |
|---|---|---|---|
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 121 °C | |
| Flow: -40 to 95 ° C | -40到95℃ | ASTME831 | 6.7E-05 cm/cm/°C |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 6.7E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 8E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 116 °C | |
| Horizontal: -40 to 95 ° C | 横向, -40到95℃ | ASTME831 | 8E-05 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9414T 7B1D086T |
|---|---|---|---|
| yield | ASTM D638 | 57.6 Mpa | |
| ASTM D638 | 5.6 % | ||
| Yield, 50.0mm span | ASTM D790 | 92.0 Mpa | |
| yield | ISO 527-2/50 | 56.8 Mpa | |
| fracture | ISO 527-2/50 | 55.3 Mpa | |
| ASTM D638 | 59.1 Mpa | ||
| ISO 527-2/50 | 110 % | ||
| ASTM D638 | 120 % | ||
| yield | ISO 527-2/50 | 5.4 % | |
| --8 | ISO 178 | 88.0 Mpa | |
| 50.0mm span | ASTM D790 | 2180 Mpa | |
| --1 | ASTM D638 | 2180 Mpa | |
| --7 | ISO 178 | 2120 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9414T 7B1D086T |
|---|---|---|---|
| transmissivity | 2000µm | 内部方法 | 84.0 % |
| Haze ratio | 2000µm | 内部方法 | 3.0 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9414T 7B1D086T |
|---|---|---|---|
| density | ASTMD792 | 1.19 g/cm³ | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 12.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.12 % |
| 平衡,23°C,50%RH | ISO 62 | 0.090 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 13 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9414T 7B1D086T |
|---|---|---|---|
| UL flame retardant rating | 1.80mm | UL 94 | V-0 |
| 1.50mm | UL 94 | V-1 | |
| Limiting Oxygen Index | ISO 4589-2 | 36 % |