PA612

PA612 Zytel® 77G33L NC010 DUPONT USA

323

Unit Price:US$ 6,283 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:wear resistant｜High impact resistance
Application Areas:Automotive Applications｜Fitness equipment｜electrical equipment
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			PA612.33％玻纤增强.注塑成型

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	70 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	60 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	23 mm/min
UL flame retardant rating	0.70mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.70mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	23 %
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1E-04 g

mechanical properties	Test Condition	Test Method	Test Result
shear strength		ASTM D732	75.0 Mpa
Tensile modulus		ISO 527-2	9500 Mpa
tensile strength	Break	ISO 527-2	170 Mpa
Tensile strain	Break	ISO 527-2	3.2 %
Bending modulus		ISO 178	8500 Mpa
bending strength		ISO 178	260 Mpa
Compressive stress		ISO 604	160 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	13 kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	80 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength		ASTM D256/ISO 179	11 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	60 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D412/ISO 527	3.2 %
Tensile modulus		ASTM D412/ISO 527	9500 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D412/ISO 527	168 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	8200 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	216 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
Glass transition temperature		ISO 11357-2	65.0 °C
Melting temperature		ISO 11357-3	218 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	1.4E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1.1E-04 cm/cm/°C
				Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	8.3E-05 cm/cm/°C
					Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.6E-04 cm/cm/°C
					Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	7.5E-08 m²/s
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	216 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	200 ℃（℉）
Melting temperature			218 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.83-1.58

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.30 %
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.8 %
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.70 %
Stickiness		ISO 307	100 cm³/g
Top out temperature			210 °C
SpecificHeatCapacity of Melt			2130 J/kg/°C
ThermalConductivityofMelt			0.26 W/m/K
Shrinkage rate	MD：3.20mm		0.20 %
	Shrinkage rate	TD：3.20mm		1.0 %
		Shrinkage rate	TD	ISO 294-4	0.90 %
		Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30 %
density		ASTM D792/ISO 1183	1.32
Shrinkage rate		ASTM D955	0.3-0.9 %
Water absorption rate		ASTM D570/ISO 62	0.7 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	-- ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric strength		IEC 60243-1	33 KV/mm
Relative permittivity	100Hz	IEC 60250	4.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.70
Dissipation factor	100Hz	IEC 60250	0.014
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.020
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		ASTM D257/IEC 60093	1.00E+12 Ω
Dielectric loss		ASTM D150/IEC 60250	4.1
Volume resistivity		ASTM D257/IEC 60093	1.00E+13 Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA612 Zytel® 77G33L NC010 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet